Smooth On Vytaflex 20

$285.00$980.00 + Gst ($313.50 - $1,078.00 AUD)

Using Smooth-On’s exclusive “V-Polymer™” technology, VytaFlex™ urethane rubbers offer superior physical and performance properties for casting concrete. VytaFlex™ mold rubbers work especially well for casting pigmented / colored concrete. Molds made with VytaFlex™ Series urethanes will render accurate and uniform colored castings.

“V-Polymer™” Technology:

Formulated Especially for Casting Concrete, Superior physical & performance properties, Long-term dimensional stability, Color-accurate castings every time, Consistent surface finish every time.

Lasting Durability: Real World Results

Concrete casting pros in the U.S. and around the world know VytaFlex™ as the industry standard for making rubber molds that have the abrasion resistance and tear strength needed to keep production moving.

Add to Wishlist
SKU: SMVYTAFLEX20 Categories: , ,
Shop for Smooth on Brand in Australia

Description

Glass Fiber Reinforced Concrete:

The versatility and durability of your VytaFlex™ rubber molds will allow you to maximize the full benefits of using FORTON™ VF‑774 Acrylic Polymer in GFRC to produce custom architectural elements.

Using Smooth-On’s exclusive “V-Polymer™” technology, VytaFlex™ urethane rubbers offer superior physical and performance properties for casting concrete. VytaFlex™ urethanes are available in 10A, 20A, 30A, 40A,  45A, 50A and 60A Shore hardness’s and feature convenient one-to-one by volume mix ratios.

Vacuum degassing is not necessary and VytaFlex™ rubbers cure with negligible shrinkage to a durable rubber that will last in production.

VytaFlex™ mold rubbers work especially well for casting pigmented / colored concrete. Molds made with VytaFlex™ Series urethanes will render accurate and uniform colored castings.

Data At-A-Glance

Mix Ratio By Volume 1A:1B
Mix Ratio By Weight 1A:1B
Pot Life 30 minutes
Cure Time 16 hours
Shore Hardness 20 A
Specific Gravity 1.00 g/cc
Specific Volume 27.7 cu. in./lb.
Color Clear Amber
Tensile Strength 200 psi
100% Modulus 50 psi
Elongation @ Break 1,000 %
Die C Tear Strength 60 pli
Shrinkage <.001 in. / in.
Mixed Viscosity 1,000 cps

Instructions

START BY PREPARING YOUR MODEL…

Preparation – Store and use at room temperature (73°F/23°C). These products have a limited shelf life and should be used as soon as possible. Use in a low humidity environment (below 50% RH). Mixing containers should have straight sides and a flat bottom. Mixing sticks should be flat and stiff with defined edges for scraping the sides and bottom of your mixing container. Good ventilation (room size) is essential. Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk.

Some Materials Must Be Sealed – Urethanes are adhesive. To prevent adhesion between the rubber and model surface, models made of porous materials (gypsum plasters, concrete, wood, stone, etc.) must be sealed prior to applying a release agent. SuperSeal™ (available from Smooth-On) or One Step™ are fast drying sealers suitable for sealing porous surfaces without interfering with surface detail. Sonite Wax™ or high-grade shellac is suitable for rough contours. A high quality Shellac is suitable for sealing modeling clays that contain sulfur or moisture (water based). Thermoplastics (polystyrene) must also be sealed with shellac or PVA. In all cases, the sealing agent should be applied and allowed to completely dry prior to applying a release agent.

Non-Porous Surfaces – Metal, glass, hard plastics, sulfur free clays, etc. require only a release agent.

Applying A Release Agent – A release agent is necessary to facilitate demolding when casting into or over most surfaces. Use a release agent made specifically for mold making (Universal™ Mold Release available from Smooth-On). A liberal coat of release agent should be applied onto all surfaces that will contact the rubber.

IMPORTANT: To ensure thorough coverage, lightly brush the release agent with a soft brush over all surfaces of the model. Follow with a light mist coating and let the release agent dry for 30 minutes. Because no two applications are quite the same, a small test application to determine suitability for your project is recommended if performance of this material is in question.


MEASURING & MIXING…

Liquid urethanes are moisture sensitive and will absorb atmospheric moisture. Mixing tools and containers should be clean and made of metal or plastic. Materials should be stored and used in a warm environment (73°F/23°C).

IMPORTANT: Stir Part B thoroughly before dispensing. After dispensing equal amounts of Parts A and B into mixing container, mix thoroughly for at least 3 minutes making sure that you scrape the sides and bottom of the mixing container several times.

If Mixing Large Quantities (16 lbs./7 kgs. or more) at one time, use a mechanical mixer (i.e. Squirrel Mixer or equal) for 3 minutes followed by careful hand mixing for one minute as directed above. Then, pour entire quantity into a new, clean mixing container and do it all over again.

Although this product is formulated to minimize air bubbles in your the cured rubber, vacuum degassing prior to pouring rubber will further reduce entrapped air.


POURING, CURING & PERFORMANCE…

For best results, pour your mixture in a single spot at the lowest point of the containment field. Let the rubber seek its level up and over the model. A uniform flow will help minimize entrapped air. The liquid rubber should level off at least 1/2” (1.3 cm) over the highest point of the model surface.

Curing – Allow rubber to cure a minimum of 16 – 24 hours at room temperature (73°F/23°C) before demolding. VytaFlex™ 10 should cure for at least 24 hours before demolding. Cure time can be reduced with mild heat or by adding Smooth-On KickIt™ Cure Accelerator. Do not cure rubber where temperature is less than 65°F/18°C.

Post Curing – Optional: Following an overnight cure, heating the rubber to 150°F (65°C) for 4 to 8 hours will increase physical properties and performance.

Using The Mold – If using as a mold material, a release agent should be applied to the mold before each casting. AquaCon™ or In & Out™ II Concrete Release Concentrate (available from Smooth-On) is recommended for releasing concrete.

Performance & Storage – Fully cured rubber is tough, durable and will perform if properly used and stored. The physical life of the rubber depends on how you use it.